Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Dissolved Volume Flow Rate (MVR) | | ASTM D1238 | 15.7 cm3/10min |
| Shrinkage rate | | ASTM D955 | 0.50 % |
| Shrinkage rate | | ASTM D955 | 0.60 % |
| Shrinkage rate | | ISO 294-4 | 0.57 % |
| Shrinkage rate | | ISO 294-4 | 0.53 % |
| Water absorption rate | | ISO 62 | 0.12 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 2550 Mpa |
| Tensile modulus | | ISO 527-2/1 | 2600 Mpa |
| tensile strength | | ASTM D638 | 67.0 Mpa |
| tensile strength | | ISO 527-2 | 62.0 Mpa |
| tensile strength | | ASTM D638 | 60.0 Mpa |
| tensile strength | | ISO 527-2 | 54.0 Mpa |
| elongation | | ASTM D638 | 4.5 % |
| elongation | | ISO 527-2 | 4.3 % |
| elongation | | ASTM D638 | 6.5 % |
| elongation | | ISO 527-2 | 6.7 % |
| Flexural modulus | | ASTM D790 | 2820 Mpa |
| Flexural modulus | | ISO 178 | 2800 Mpa |
| bending strength | | ASTM D790 | 103 Mpa |
| bending strength | | ISO 178 | 102 Mpa |
| Friction coefficient 3 | | ASTM D3702 | 0.090 |
| Friction coefficient 3 | | ASTM D3702 | 0.22 |
| Wear factor 3 | | ASTM D3702 | 6.0E+6 10^-8 mm³/N·m |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| | ASTM D4812 | 1600 J/m |
| | ISO 180/1U | 100 kJ/m² |
| Dart impact equipped with measuring instruments | | ASTM D3763 | 51.0 J |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 80 °C |
| drying time | | | 4.0 到 6.0 hr |
| Suggested maximum moisture content | | | 0.020 % |
| Temperature at the rear of the barrel | | | 250 到 260 °C |
| Temperature in the middle of the barrel | | | 255 到 265 °C |
| Temperature at the front of the material cylinder | | | 260 到 270 °C |
| Processing (melt) temperature | | | 255 到 290 °C |
| Temperature | | | 40 到 65 °C |
| Back pressure | | | 0.200 到 0.300 Mpa |
| screw speed | | | 30 到 60 rpm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Thermal deformation temperature under load | | ASTM D648 | 97.0 °C |
| Thermal deformation temperature under load | | ASTM D648 | 89.0 °C |
| Thermal deformation temperature under load | | ISO 75-2/Af | 94.0 °C |
| | ASTM E831, ISO 11359-2 | 6.6E-5 cm/cm/°C |
| | ASTM E831 | 6.7E-5 cm/cm/°C |
| | ISO 11359-2 | 6.7E-5 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.