PA6 SLOVAMID® 6 LI/1
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO1183 | 1.10 g/cm³ | |
| melt mass-flow rate | ISO1133 | 10 g/10min | |
| Shrinkage rate | STM640808 | 2.0 % | |
| STM640808 | 2.1 % | ||
| water content | ISO960 | 0.20 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot filament ignition temperature | IEC60695-2-13 | 850 °C | |
| UL flame retardant rating | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile stress | Yield | ISO527-2 | 65.0 MPa |
| Tensile strain | Yield | ISO527-2 | 4.0 % |
| Flexural modulus | ISO178 | 2400 MPa | |
| Bending stress | ISO178 | 95.0 MPa | |
| Tensile modulus | ISO527-2 | 2750 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO179 | 8.0 kJ/m² | |
| ISO179 | 11 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO179 | 无断裂 | |
| ISO179 | 无断裂 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO75-2/B | 68.0 °C | ||
| vicat | ISO306/B | 218 °C | |
| ISO3146 | 222 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.