Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.55 g/cm³ |
| Water absorption rate | | ISO 62 | 0.37 % |
| Water absorption rate | | ISO 62 | 0.18 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1 | 10000 MPa |
| tensile strength | | ISO 527-2/5 | 140 MPa |
| Tensile strain | | ISO 527-2/5 | 2.6 % |
| bending strength | | ISO 178 | 210 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 10 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 11 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 55 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 60 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 9.0 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 10 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | >1.0E+14 ohms |
| Volume resistivity | | IEC 60093 | >1.0E+16 ohms·cm |
| | IEC 60250 | 4.10 |
| Dissipation Factor | | IEC 60250 | 0.017 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 2 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Hot deformation temperature (HDT) | | ISO 75-2/B | 220 °C |
| Hot deformation temperature (HDT) | | ISO 75-2/A | 202 °C |
| melting temperature | | ISO 3146 | 235 °C |
| | DIN 53752 | 3.5E-05 cm/cm/°C |
| | DIN 53752 | 9.5E-05 cm/cm/°C |
| maximum service temperature | | IEC 216 | 140 °C |
| maximum service temperature | | | 160 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.