PA66 13G50 BK ASAHI JAPAN

Form：Granules | Grade：Injection grade

Properties:

Fatigue resistanceHigh rigidityCreep resistancehigh strength

Typical Applications:

Electrical applicationsAutomotive ApplicationsGears

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electrical applications \| Automotive Applications \| Gears
Properties:	Fatigue resistance \| High rigidity \| Creep resistance \| high strength

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch		ISO 179	无断裂
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.75 mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Taber abraser	1000 Cycles	ASTM D1044	--	mg
bending strength	23°C	ISO 178	371	Mpa
bending strength	bending strength	--	ASTM D790	390	Mpa
Bending modulus	23°C	ISO 178	13600	Mpa
Bending modulus	Bending modulus	--	ASTM D790	14500	Mpa
elongation	Break, 23°C	ISO 527-2	2.0	%
elongation	elongation	Break	ASTM D638	2.5	%
tensile strength	--	ASTM D638	235	Mpa
tensile strength	tensile strength	Break, 23°C	ISO 527-2	237	Mpa
Tensile modulus	23°C	ISO 527-2	16900	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
thermal conductivity			0.40	W/m/K
Linear coefficient of thermal expansion	Flow	ASTM D696	2.0E-5	cm/cm/°C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	255	°C
	Hot deformation temperature	1.8 MPa, Unannealed	ASTM D648	250	°C
	Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed	ASTM D648	260	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	--	%
Water absorption rate	Water absorption rate	Saturation, 23°C		--	%
Shrinkage rate	Flow	Internal Method	0.40	%
Shrinkage rate	Shrinkage rate	横向Flow	Internal Method	0.70	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		ASTM D257	1.0E+15	ohms
Volume resistivity	--	ASTM D257	1.0E+15	ohms·cm
Volume resistivity	Volume resistivity	23°C	IEC 60093	1.0E+15	ohms·cm
Dielectric strength		ASTM D149	21	KV/mm
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	118
	Rockwell hardness	M-Scale	ASTM D785	95
		Rockwell hardness	R -Sale	ISO 2039-2	118
		Rockwell hardness	Rockwell hardness	M -Sale	ISO 2039-2	95

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PA66 13G50 BK ASAHI JAPAN

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index