POM UV90Z CELANESE USA

Form：Granules | Grade：Injection grade

Properties:

Weather resistanceHigh mobilityUV resistanceAutomotive interior parts

Typical Applications:

Automotive Applicationspipeline

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive Applications \| pipeline
Properties:	Weather resistance \| High mobility \| UV resistance \| Automotive interior parts

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179/1eA	6.0	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	100	kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	5.7	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2/1A/1	2700	Mpa
tensile strength	Yield,23°C	ASTM D638	60.7	Mpa
tensile strength	tensile strength	Yield	ISO 527-2/1A/50	64.0	Mpa
Tensile strain	Yield	ISO 527-2/1A/50	9.0	%
Bending modulus	23°C	ISO 178	2470	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	155	°C
	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	110	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	91.0	°C
Melting temperature		ASTM D3418	165	°C
Melting temperature	Melting temperature		ISO 11357-3	165	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	1.1E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	1.2E-04	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	TD	ISO 294-4	1.7	%
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	1.9	%
Water absorption rate	Saturation,23°C	ISO 62	0.75	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.20	%
density		ASTM D792	1.41	g/cm³
density	density		ISO 1183	1.41	g/cm³
Melt Volume Flow Rate (MVR)	190°C/2.16kg	ISO 1133	8.00	cm3/10min
Shrinkage rate	MD	ASTM D955	2.2	%
Shrinkage rate	Shrinkage rate	TD	ASTM D955	1.8	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.