Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | 内部方法 | 1.1 % |
| Water absorption rate | | ASTMD570 | 2.4 % |
| density | | ASTMD792 | 1.37 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | Break | ASTMD638 | 4.2 % |
| Flexural modulus | | ASTMD790 | 3500 MPa |
| bending strength | | ISO 178 | 100 MPa |
| bending strength | Break | ASTM D790 | 100 MPa |
| tensile strength | Break | ASTMD638 | 80.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179 | 50 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTMD257 | 1E+15 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTMD648 | 225 °C |
| Heat distortion temperature | | ASTMD648 | 90.0 °C |
| melting temperature | | ASTMD2117 | 260 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 6E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare