PA6

PA6 MAZMID B 150 FV 25 Mazzaferro Indústria e Comércio de Polímeros e Fibras Ltda.

Properties:
Filler glass fiber reinforced material 25% filler by weight
Usages:
Shell electrical electronic application fields electrical components gears automotive applications knobs
Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap		J/m	110 170

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.6mm		HB --

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		MPa	7000 4500
tensile strength		MPa	135 85.0
elongation	Break	%	3.5 5.5
Bending modulus		MPa	6500 400
bending strength		MPa	210 120

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	MD	cm/cm/°C	3E-05 --
Hot deformation temperature	0.45MPa,Unannealed	°C	195 --
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	°C	180 --
Continuous use temperature		°C	100to110 --
Melting temperature		°C	214to220 --

Physical properties	Test Condition	Test Method	Test Result
density		g/cm³	1.32 --
Shrinkage rate	MD	%	0.35to0.55 --
Water absorption rate	23°C,24hr	%	1.0 --

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		ohms·cm	1E+15 --
Dielectric strength		kV/mm	22 --

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale		122 110

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.