PA66 A3GK30 AKRO-PLASTIC GERMANY

Form：Granules

Properties:

Excellent appearanceGlass bead reinforcementLow warpageenhanceFiller: Glass beads30%Filler by weight

Typical Applications:

ShellHousehold appliancesElectronic fieldElectrical fieldElectrical appliances

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Shell \| Household appliances \| Electronic field \| Electrical field \| Electrical appliances
Properties:	Excellent appearance \| Glass bead reinforcement \| Low warpage \| enhance \| Filler: Glass beads \| 30% \| Filler by weight

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	28	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	22	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning wire flammability index	1.6mm	IEC 60695-2-12	650	°C
UL flame retardant rating	1.6mm	UL 94	HB
Burning rate	1.00mm	FMVSS302	<100	mm/min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Fracture bending strain		ISO 178	6.5	%
bending strength		ISO 178	140	Mpa
Tensile strain	Break	ISO 527-2/5	4.0	%
tensile strength	Break	ISO 527-2/5	90.0	Mpa
Tensile modulus		ISO 527-2/1	5000	Mpa
Bending modulus		ISO 178	4300	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Melting temperature		DIN EN11357-1	262	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	100	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	225	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Hygroscopicity	70°C，62%RH	ISO 1110	2.0	%
Water absorption rate	Saturation,23°C	ISO 62	5.8	%
Shrinkage rate	MD	ISO 294-4	1.2	%
Shrinkage rate	Shrinkage rate	TD	ISO 294-4	1.3	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 1
Volume resistivity		IEC 60093	1E+15	ohms·cm
Surface resistivity		IEC 60093	1E+13	ohms
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
ReinforcementContent		ISO 1172	30	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.