Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 0.900 g/cm³ |
| melt mass-flow rate | | ISO1133 | 7.0 g/10min |
| SpiralFlow | | 内部方法 | 46.0 cm |
| Shrinkage rate | | 内部方法 | 1.0到1.4 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO2039-2 | 75 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| Gardner glossiness | | ASTMD523 | 90 |
| Haze ratio | | ISO14782 | 15 % |
| Haze ratio | | ISO14782 | 50 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | Yield | ISO527-2 | 22.0 MPa |
| Nominal tensile fracture strain | | ISO527-2 | >400 % |
| Tensile modulus | | ISO527-2 | 800 MPa |
| Flexural modulus | | ISO178 | 750 MPa |
| Bending stress | | ISO178 | 25.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179 | 2.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179 | 8.0 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 70.0 °C |
| vicat | | ISO306 | 110 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare