Unspecified Generic PP, Unspecified - Glass Fiber, Long

Properties:
Filler
long glass fiber
Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
Water absorption rate		ASTM D570	0.020to0.060 %
density		ASTM D792	0.180to1.35 g/cm³
density	density		ISO 1183	1.04to1.48 g/cm³
Shrinkage rate		ASTM D955	0.020to0.31 %
	Shrinkage rate		ASTM D955	0.29to0.61 %
	Shrinkage rate	Shrinkage rate		ISO 294-4	0.080to0.70 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness		ASTM D785	105to121

Mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	560to10900 MPa
Tensile modulus	Tensile modulus		ISO 527-2	4280to14000 MPa
tensile strength		ASTM D638	73.5to148 MPa
	tensile strength		ISO 527-2	96.1to122 MPa
		tensile strength		ASTM D638	97.0to131 MPa
			tensile strength		ISO 527-2	82.6to151 MPa
			tensile strength	tensile strength		ASTM D638	5.00to126 MPa
elongation		ASTM D638	1.8to3.0 %
elongation	elongation		ISO 527-2	1.7to2.6 %
Flexural modulus		ASTM D790	3330to9450 MPa
Flexural modulus	Flexural modulus		ISO 178	3810to11400 MPa
bending strength		ASTM D790	150to190 MPa
bending strength	bending strength		ISO 178	108to288 MPa
		ASTM D1894	0.34to0.52

Impact resistance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength		ISO 180	44to66 kJ/m²
Dart impact		ASTM D3763	1.50to16.3 J
Dart impact	Dart impact		ISO 6603-2	5.59to13.1 J
Charpy Notched Impact Strength		ISO 179	12to33 kJ/m²
Impact strength of simply supported beam without notch		ISO 179	39to75 kJ/m²
Impact strength of cantilever beam gap		ASTM D256	150to300 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ISO 180	17to29 kJ/m²
Suspended wall beam without notch impact strength		ASTM D256	740to770 J/m

Thermal performance	Test Condition	Test Method	Test Result
		ISO 11359-2	4.6E-5到8.3E-5 cm/cm/°C
Hot deformation temperature (HDT)		ISO 75-2/B	162to164 °C
	Hot deformation temperature (HDT)		ASTM D648	149to158 °C
		Hot deformation temperature (HDT)		ISO 75-2/A	155to161 °C
		Hot deformation temperature (HDT)	Hot deformation temperature (HDT)		ISO 75-2/C	122to138 °C
vicat		ISO 306	145to166 °C
melting temperature		ISO 11357-3	165to166 °C
		ASTM D696	2.2E-5到6.8E-5 cm/cm/°C
			ASTME831	1.8E-5到4.7E-5 cm/cm/°C
				ISO 11359-2	3.3E-5到4.6E-5 cm/cm/°C
					ASTME831	4.5E-5到8.3E-5 cm/cm/°C
Hot deformation temperature (HDT)		ASTM D648	158to165 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.