Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.41 g/cm³ |
| Shrinkage rate | | ASTM D955 | 0.20to0.30 % |
| Shrinkage rate | | ASTM D955 | 0.50to0.70 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTM D785 | 84 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-2 |
| UL flame retardant rating | | UL 94 | V-2 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | ASTM D790 | 185 MPa |
| tensile strength | | ASTM D638 | 112 MPa |
| elongation | Break | ASTM D638 | 5.0 % |
| Flexural modulus | | ASTM D790 | 9500 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 80 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 1E+16 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 130 °C |
| Heat distortion temperature | | ASTM D648 | 118 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.