Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| spiral flow length | | 内部方法 | 72.0 CM |
| Shrinkage rate | | ISO 294-4 | 1.2 % |
| Shrinkage rate | | ISO 294-4 | 0.20 % |
| Water absorption rate | | ISO 62 | 4.3to4.7 % |
| moisture absorption | | ISO 1110 | 1.7to1.9 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | ISO 2039-1 | 270 Mpa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | FMVSS302 | <100 mm/min |
| UL flame retardant rating | | UL 94 | HB |
| Burning wire flammability index | | IEC 60695-2-12 | 650 °C |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ReinforcementContent | | ISO 1172 | 40 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 95 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 100 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1 | 13100 Mpa |
| tensile strength | | ISO 527-2/5 | 225 Mpa |
| Tensile strain | | ISO 527-2/5 | 3.0 % |
| Flexural modulus | | ISO 178 | 12000 Mpa |
| bending strength | | ISO 178 | 360 Mpa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1E+12 ohms |
| Volume resistivity | | IEC 60093 | 1E+13 ohms·cm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 260 °C |
| Heat distortion temperature | | ISO 75-2/A | 260 °C |
| Heat distortion temperature | | ISO 75-2/C | 225 °C |
| melting temperature | | DIN EN11357-1 | 262 °C |
| TemperatureIndex | | IEC 216 | 130to150 °C |
| TemperatureIndex | | IEC 216 | 160to175 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.