Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.90到2.10 g/cm³ |
| Apparent density | | ISO60 | 0.75到0.90 g/cm³ |
| Shrinkage rate | | ISO2577 | 0.30到0.40 % |
| Shrinkage rate | | ISO2577 | 0.50到0.60 % |
| Water absorption rate | | ISO62 | <0.20 % |
| PostShrinkage | | ISO2577 | <0.050 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Burning wire flammability index | | IEC60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 930 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | Compression Molded | ISO178 | 8000到12000 MPa |
| Flexural modulus | Injection | ISO178 | 13000到16000 MPa |
| Bending stress | Compression Molded | ISO178 | 80.0到100 MPa |
| Bending stress | Injection | ISO178 | 100到140 MPa |
| compression stress | | ISO604 | 150到200 MPa |
| Tensile stress | | ISO527-2 | 35.0到60.0 MPa |
| Tensile stress | Injection | ISO527-2 | 40.0到70.0 MPa |
| Tensile modulus | Compression Molded | ISO527-2 | 6000到9000 MPa |
| Tensile modulus | Injection | ISO527-2 | 9000到11000 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | Compression Molded | ISO179/1eA | 2.5到3.5 kJ/m² |
| Charpy Notched Impact Strength | Injection | ISO179/1eA | 3.5到5.0 kJ/m² |
| Impact strength of simply supported beam without notch | Compression Molded | ISO179/1eU | 5.0到10 kJ/m² |
| Impact strength of simply supported beam without notch | Injection | ISO179/1eU | 8.0到11 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| arc resistance | | ASTMD495 | PLC 4 |
| CTI | | IEC60112 | 600 V |
| Surface Resistivity | | IEC60093 | 1.0E+14到1.0E+15 ohms |
| Volume resistivity | | IEC60093 | 1.0E+14到1.0E+15 ohms·cm |
| dielectric strength | | IEC60243-1 | 35到40 kV/mm |
| | IEC60250 | 4.505.00 |
| | IEC60250 | 4.004.50 |
| Dissipation Factor | | IEC60250 | 0.010到0.030 |
| Dissipation Factor | | IEC60250 | 0.010到0.030 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | >200 °C |
| | ISO75-2/C | >180 °C |
| | ISO11359-2 | 5.0E-6到1.0E-5 cm/cm/°C |
| thermal conductivity | | ASTME1461 | 0.90到1.1 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.