ASA+PC Infino WR-7000P
0
- Properties:Mechanical properties
CompareTechnical Data Sheet
| Test Condition | Test Method | Test Result | |
|---|---|---|---|
| tensile strength | Break | ISO 527-2/50 | 55.0 MPa |
| elongation | Break | ASTM D638 | 60 % |
| Tensile strain | Break | ISO 527-2/50 | 60 % |
| Flexural modulus | ASTM D790 | 2300 MPa | |
| ISO 178 | 2200 MPa | ||
| bending strength | ASTM D790 | 80.0 MPa | |
| ISO 178 | 87.0 MPa | ||
| density | ASTM D792 | 1.14 g/cm³ | |
| ISO 1183 | 1.14 g/cm³ | ||
| melt mass-flow rate | ASTM D1238 | 34 g/10min | |
| ISO 1133 | 34 g/10min | ||
| Shrinkage rate | ASTM D955 | 0.40to0.70 % | |
| ASTM D955 | 0.40to0.70 % | ||
| ISO 2577 | 0.40to0.70 % | ||
| ISO 2577 | 0.40to0.70 % | ||
| Heat distortion temperature | ISO 75-2/B | 115 °C | |
| tensile strength | Yield | ASTM D638 | 58.0 MPa |
| Yield | ISO 527-2/50 | 57.0 MPa | |
| Break | ASTM D638 | 54.0 MPa | |
| Tensile modulus | ASTM D638 | 2300 MPa | |
| ISO 527-2/50 | 2000 MPa | ||
| Heat distortion temperature | ASTM D648 | 105 °C | |
| Impact strength of cantilever beam gap | ISO 180/1A | 42 kJ/m² | |
| Rockwell hardness | R-Scale | ASTM D785 | 111 |
| R-Scale | ISO 2039-2 | 111 | |
| Heat distortion temperature | ASTM D648 | 116 °C | |
| ISO 75-2/A | 97.0 °C | ||
| vicat | ISO 306/B50 | 114 °C | |
| Charpy Notched Impact Strength | ISO 179/1eA | 43 kJ/m² | |
| Impact strength of cantilever beam gap | ASTM D256 | 150 J/m | |
| ASTM D256 | 79 J/m | ||
| ASTM D256 | 450 J/m | ||
| ASTM D256 | 140 J/m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.