PA12 LUVOCOM® 6-8660

Usages:
Roller
business equipment
handles
automotive applications
profiles
textile applications
engineering accessories
Compare

Technical Data Sheet

physical property	Test Method	Test Result
density	ISO1183	1.03 g/cm³
Melt volume flow rate	ISO1133	13.0 cm³/10min
Shrinkage rate	DIN16901	0.70到1.0 %
Water absorption rate		<0.10 %

Mechanical properties	Test Condition	Test Method	Test Result
Bending stress		ISO178	50.0 MPa
Bending Strain		ISO178	7.2 %
Tensile modulus		ISO527-2	1300 MPa
Tensile stress	Break	ISO527-2	42.0 MPa
Tensile strain	Yield	ISO527-2	6.5 %
Flexural modulus		ISO178	1100 MPa

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO179/1eA	16 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO179/1eA	38 kJ/m²
Impact strength of simply supported beam without notch		ISO179/1fU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch		ISO179/1fU	无断裂

Electrical performance	Test Condition	Test Method	Test Result
Surface Resistivity		IEC60093	<1.0E+13 ohms
insulation resistance		IEC60167	1.0E+9到1.0E+12 ohms

Thermal performance	Test Condition	Test Method	Test Result
Maximum operating temperature - SharrTerm			140 °C
Continuous use temperature		UL746B	90.0 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.