Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | | 1.85 g/cm³ |
| Tightening rate | | | 2.0到5.0 |
| Shrinkage rate | | | 0.20到0.40 % |
| Water absorption rate | | | 0.25 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Barcol Hardness | | | 65 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | | 82.7 MPa |
| Flexural modulus | | | 13800 MPa |
| bending strength | | | 103 MPa |
| compressive strength | | | 193 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | | 27 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | | 1E+15 ohms |
| Volume resistivity | | | 1E+15 ohms·cm |
| dielectric strength | | | 14 kV/mm |
| dielectric constant | | | 3.90 |
| dielectric constant | | | 4.30 |
| Dissipation Factor | | | 0.012 |
| Dissipation Factor | | | 0.011 |
| Dissipation Factor | | | 180 sec |
| Dissipation Factor | | | 56000 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | | 0.67 W/m/K |
| Linear coefficient of thermal expansion | | | 260 °C |
| Glass Transition Temperature | | | 175 °C |
| | | 2.5E-05 cm/cm/°C |
| | | 7E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.