Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Melt volume flow rate | | ISO 1133 | 17 CM |
| Shrinkage rate | | | 0.3/1.1 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.45 g/cm |
| Water absorption rate | | | 0.2 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation at yield | | ISO 899-1 | 3 % |
| Charpy Notched Impact Strength | | ISO 179/1eU | 8 KJ/m |
| Tensile stress | | ISO 527-2 | 120 Mpa |
| Tensile modulus | | ISO 527-2 | 7100 Mpa |
| ball-indentation hardness | | ISO 2039-1 | 180 Mpa |
| bending strength | | ISO 178 | 170 Mpa |
| Charpy Notched Impact Strength | | ISO 179/1eU | 58 KJ/m |
| Other performance | Test Condition | Test Method | Test Result |
|---|
| Short term temperature index | | IEC 216-1 | 140/140 °C |
| Water absorption rate | | DIN 53496 | 0.4 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Relative Arc Track Index Mathematics/CTI | | IEC 112 | CT1300 |
| loss angle | | IEC 250 | 0.0015 |
| Volume resistivity | | IEC 93 | 10 Ω.cm |
| Surface Resistivity | | IEC 93 | 10 Ω |
| Conductivity | | DIN 52612 | 0.27 w/mk |
| specific heat | | | 1.6 J/gk |
| dielectric constant | | IEC 250 | 3.7 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| maximum service temperature | | | 210 °C |
| melting temperature | | ISO 3146 | 220-225 °C |
| Heat distortion temperature | | ISO 75-2 | 205 °C |
| combustibility | | UL 94 | HB |
| Linear coefficient of thermal expansion | | DIN 53752 | 3-4 |
| Heat distortion temperature | | ISO 75-2 | 220 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.