impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂

squeeze out	Test Condition	Test Method	Test Result
Melt Temperature			190 to 220 °C
drying time			4.0 to 8.0 hr
drying temperature			55 to 65 °C

mechanical properties	Test Condition	Test Method	Test Result
Tensile strain	Break	ISO 527-2	> 300 %
tensile strength	50% Strain	ISO 527-2	-- Mpa
tensile strength	tensile strength	Break	ISO 527-2	30.0 Mpa
Tensile modulus		ISO 527-2	-- Mpa

injection	Test Condition	Test Method	Test Result
Mold temperature			10 to 30 °C
Processing (melt) temperature			180 to 260 °C
drying time			4.0 to 8.0 hr
drying temperature			55 to 65 °C

thermal performance	Test Condition	Test Method	Test Result
Melting temperature	Renewable Carbon Conent	CSA LISTED	28 to 32 %
Melting temperature	Melting temperature		ISO 11357-3	135 °C
Vicat softening temperature		ISO 306/B50	81.0 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.50 %
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	1.3 %
Shrinkage rate	Flow	ISO 294-4	0.60 %
Shrinkage rate	Shrinkage rate	横向Flow	ISO 294-4	0.60 %

hardness	Test Condition	Test Method	Test Result
Shore hardness	Shore D, 15 Sec	ISO 7619-1	25

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.