Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | % | 0.40 -- |
| Shrinkage rate | | % | 0.10 -- |
| Water absorption rate | | % | 5.0 -- |
| Water absorption rate | | % | 1.5 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | MPa | 130 90.0 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Flammability level | | | HB -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | MPa | 6900 5200 |
| Tensile stress | | MPa | 110 90.0 |
| Tensile strain | | % | 3.0 5.0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | kJ/m² | 35 |
| Impact strength of simply supported beam without notch | | kJ/m² | 40 45 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ohms·cm | 1E+14 |
| dielectric strength | | kV/mm | 40 34 |
| CTI | | V | -- 600 |
| Surface Resistivity | | ohms | -- 1E+12 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | °C | 155 -- |
| | °C | 70.0 -- |
| Continuous use temperature | | °C | 80.0到110 -- |
| Continuous use temperature | | °C | 160 -- |
| Melting temperature 4 | | °C | 222 -- |
| | cm/cm/°C | 2.5E-05 -- |
| | cm/cm/°C | 1.5E-04 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.