Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 2.5 g/10min |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | ASTM D-2457 | 90 |
| Haze ratio | | ASTM D-1003 | 2.6 % |
| gloss | | ASTM D2457 | 90 |
| Haze ratio | | ASTM D1003 | 2.6 % |
| processability | Test Condition | Test Method | Test Result |
|---|
| Melt Temperature | | | 274 °C |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D-792 | 0.935 g/m3 |
| melt mass-flow rate | | ASTM D-1238 | 2.5 g/10min |
| film thickness | | | 25.4 um |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D-882 | 17.6 Mpa |
| tensile strength | | ASTM D-882 | 16.9 Mpa |
| tensile strength | | ASTM D-882 | 39.9 Mpa |
| tensile strength | | ASTM D-882 | 59.2 Mpa |
| elongation at break | | ASTM D-882 | 620 % |
| elongation at break | | ASTM D-882 | 750 % |
| Dart impact | | ASTM D-1709A | 57 g |
| Elmendorf tear strength | | ASTM D-1922 | 83 g |
| Elmendorf tear strength | | ASTM D-1922 | 290 g |
| Other performance | Test Condition | Test Method | Test Result |
|---|
| Thin film puncture strength | | 内部方法 | 10.3 J/cm³ |
| Film toughness | | ASTM D-882 | 324 J/cm³ |
| Film toughness | | ASTM D-882 | 308 J/cm4 |
| film | Test Condition | Test Method | Test Result |
|---|
| elongation | | ASTM D882 | 620 % |
| elongation | | ASTM D882 | 750 % |
| Dart impact | | ASTM D1709A | 57 g |
| Elmendorf tear strength | | ASTM D1922 | 83 g |
| Elmendorf tear strength | | ASTM D1922 | 290 g |
| film thickness | | | 25 µm |
| Thin film puncture strength | | 内部方法 | 10.3 J/cm³ |
| film strength | | ASTM D882 | 324 J/cm³ |
| film strength | | ASTM D882 | 308 J/cm³ |
| tensile strength | | ASTM D882 | 16.9 Mpa |
| tensile strength | | ASTM D882 | 17.6 Mpa |
| tensile strength | | ASTM D882 | 59.2 Mpa |
| tensile strength | | ASTM D882 | 39.9 Mpa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ASTM D-1525 | 119 °C |
| melting temperature | | 内部方法 | 125 °C |
| vicat | | ASTM D1525 | 119 °C |
| melting temperature | | 内部方法 | 125 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.