Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.40 g/cm³ |
| Shrinkage rate | | ISO 2577 | 1.8to3.0 % |
| Water absorption rate | | ISO 62 | 0.80 % |
| Water absorption rate | | ISO 62 | 0.20 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | ISO 1210 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | ISO 527-2 | <60.0 MPa |
| Tensile strain | Break | ISO 527-2 | >20 % |
| Flexural modulus | | ISO 178 | 2100 MPa |
| bending strength | | ISO 178 | 70.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180/1A | 7.5 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180/1U | 70 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTM D257 | 1E+14 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 105 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| RTI Imp | | UL 746 | 90.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.