Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.14 g/cm³ |
| Shrinkage rate | | ISO 294-4 | 1.4 % |
| Shrinkage rate | | ISO 294-4 | 1.4 % |
| Water absorption rate | | ISO 15512 | 0.30 % |
| relative viscosity | | ISO 307 | 2.7 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO 2039-2 | 120 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| Yellowness Index | | ASTM D1925 | -3.3 YI |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-2 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180 | 4.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 3100 Mpa |
| tensile strength | | ISO 527-2 | 86.0 Mpa |
| Nominal tensile fracture strain | | ISO 527-2 | 25 % |
| Flexural modulus | | ISO 178 | 2700 Mpa |
| bending strength | | ISO 178 | 100 Mpa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1E+12 ohms |
| Volume resistivity | | IEC 60093 | 1E+14 ohms·cm |
| dielectric strength | | IEC 60243-1 | 32 KV/mm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 200 °C |
| Heat distortion temperature | | ISO 75-2/A | 70.0 °C |
| melting temperature | | ISO 11357-3 | 260 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.