PP HP400H LYONDELLBASELL SAUDI

Form：Granules | Grade：Extrusion grade

Properties:

ProcessabilityHomopolymerChemical resistanceLow odorExtrusion stage

Typical Applications:

containertapeMonofilamentbottleHousehold goods

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	container \| tape \| Monofilament \| bottle \| Household goods
Properties:	Processability \| Homopolymer \| Chemical resistance \| Low odor \| Extrusion stage

Certificates

No Data...

Technical Data Sheet

Basic Performance	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	0.9	g/cm³
melt mass-flow rate	230℃，2.16kg	ISO 1133	2	g/10min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
elongation	Break	ISO 527-1	>50	%
Charpy Notched Impact Strength	23℃,Type 1,Edgewise,Notch A	ISO 179	4	Kj/cm2
Impact strength of simply supported beam without notch	0℃,Type 1,Edgewise	ISO 179	90	Kj/cm2
Ball Pressure Test	H 358/30	ISO 2039-1	70	Mpa
tensile strength	Yield	ISO 527-1	34	Mpa
Impact strength of simply supported beam without notch	23℃,Type 1,Edgewise	ISO 179	No Break	Kj/cm2
Bending modulus		ISO 527-1	1400	Mpa
elongation at yield		ISO 527-1	11	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa Unannealed	ISO 527-1	80	°C
Vicat softening temperature	B50(50℃/h 50N)	ISO 306	80	°C
Vicat softening temperature	Vicat softening temperature	A50(50℃/h 10N)	ISO 306	150	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.