PA66 A218G1V30 BK SOLVAY FRANCE

Form：Granules | Grade：Injection grade

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	85	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Extreme Oxygen Index		ISO 4589-2	23	%
Burning wire flammability index	1.6 mm	IEC 60695-2-12	650	°C
UL flame retardant rating	1.6 mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	23°C	ISO 178	290	Mpa
bending strength	bending strength	23°C	ASTM D790	275	Mpa
Bending modulus	23°C	ISO 178	9000	Mpa
Bending modulus	Bending modulus	23°C	ASTM D790	9700	Mpa
Tensile strain	Break, 23°C	ISO 527-2	3.2	%
tensile strength	Break, 23°C	ISO 527-2/1A	190	Mpa
Tensile modulus	23°C	ISO 527-2/1A	10000	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
Temperature in the middle of the barrel			275 to 285	°C
Temperature at the rear of the barrel			270 to 280	°C
Suggested maximum moisture content			0.15	%
drying temperature			80	°C
Temperature at the front of the material cylinder			280 to 290	°C
Mold temperature			70 to 100	°C
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Melting temperature		ISO 11357-3	263	°C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/Af	250	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	1.7	%
	Water absorption rate	Saturation, 23°C	ISO 62	5.3	%
	Water absorption rate	Water absorption rate	24 hr, 23°C	ISO 62	0.80	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index	Solution A	IEC 60112	PLC 1
Dissipation factor		IEC 60250	0.010
Dielectric strength	2.00 mm	IEC 60243-1	34	KV/mm
Volume resistivity		IEC 60093	1.0E+15	ohms·cm
Surface resistivity		IEC 60093	6.0E+15	ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.