Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 294-4 | 0.90 % |
| Shrinkage rate | | ISO 294-4 | 0.50 % |
| Water absorption rate | | ISO 62 | 1.2 % |
| other | Test Condition | Test Method | Test Result |
|---|
| purpose | | | 车辆配件 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1 | 6000 Mpa |
| Tensile stress | | ISO 527-2/5 | 110 Mpa |
| Tensile strain | | ISO 527-2/5 | 4.0 % |
| Bending modulus 3 | | ISO 178 | 5000 Mpa |
| Bending stress 3 | | ISO 178 | 170 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 40 kJ/m² |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 80 °C |
| Drying time - vacuum dryer | | | 2.0 到 6.0 hr |
| Processing (melt) temperature | | | 265 到 280 °C |
| Temperature | | | 80 到 120 °C |
| Residual Moisture Content | | Karl Fisher | < 0.10 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO 75-2/B | 215 °C |
| | ISO 75-2/A | 205 °C |
| Melting temperature 4 | | ISO 11357-3 | 220 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.