LLDPE 2645G STYRON US

Form：Granules | Grade：Blow molding grade

Properties:

High mobilityHigh rigidity

Typical Applications:

film

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	film
Properties:	High mobility \| High rigidity

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
turbidity	50.8um	ASTM D-1003	12	%
gloss	45°，50.8um	ASTM D-2457	63
gloss	gloss	45°,50.8μm	ASTM D2457	63
turbidity	50.8μm	ASTM D1003	12	%
Other performance	Test Condition	Test Method	Test Result	Test Unit
Thin film puncture strength	50.8um	Internal Method	16.6	J/cm³
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
film thickness			50.8	um
melt mass-flow rate	190℃/2.16kg	ASTM D-1238	0.9	g/10min
density		ASTM D-792	0.919	g/m3
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Elmendorf tear strength	50.8um，MD	ASTM D-1922	720	g
Elmendorf tear strength	Elmendorf tear strength	50.8um，TD	ASTM D-1922	1000	g
Dart impact	50.8um	ASTM D-1709A	300	g
Elongation at Break	50.8um，MD	ASTM D-882	620	%
Elongation at Break	Elongation at Break	50.8um，TD	ASTM D-882	740	%
Secant modulus	2% Secant，50.8um，TD	ASTM D-882	238	Mpa
Secant modulus	Secant modulus	2% Secant，50.8um，MD	ASTM D-882	168	Mpa
tensile strength	50.8um，MD,Break	ASTM D-882	48.8	Mpa
	tensile strength	50.8um，TD,Break	ASTM D-882	39.2	Mpa
		tensile strength	50.8um，Yield,TD	ASTM D-882	14.6	Mpa
		tensile strength	tensile strength	50.8um，Yield,MD	ASTM D-882	14.2	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature		ASTM D-1525	107	°C
Melting temperature		Internal Method	120	°C
Vicat softening temperature		ASTM D1525	107	°C
Melting temperature		Internal Method	120	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	190°C/2.16kg	ASTM D1238	0.90	g/10min
film	Test Condition	Test Method	Test Result	Test Unit
elongation	TD:Break,51μm	ASTM D882	740	%
Dart impact	51μm	ASTM D1709A	300	g
elongation	MD:Break,51μm	ASTM D882	620	%
tensile strength	TD:Break,51μm	ASTM D882	39.2	Mpa
	tensile strength	MD:Break,51μm	ASTM D882	48.8	Mpa
		tensile strength	TD:Yield,51μm	ASTM D882	14.6	Mpa
		tensile strength	tensile strength	MD:Yield,51μm	ASTM D882	14.2	Mpa
Elmendorf tear strength	MD:51μm	ASTM D1922	720	g
Elmendorf tear strength	Elmendorf tear strength	TD:51μm	ASTM D1922	1000	g
film thickness			51	µm
Thin film puncture strength	51μm	Internal Method	16.6	J/cm³
Secant modulus	2%Secant,MD:51μm	ASTM D882	168	Mpa
Secant modulus	Secant modulus	2%Secant,TD:51μm	ASTM D882	238	Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.