PA66 22HSP BK BASF KOREA

Form：Granules

Properties:

Chemical resistanceHigh rigiditywear resistantOil resistanthigh strengthThermal stabilityHigh toughness

Typical Applications:

Industrial applicationsElectrical applicationsAutomotive ApplicationsIndustrial machineryFitness equipmentLaptop caseBushingShellCambearing

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Industrial applications \| Electrical applications \| Automotive Applications \| Industrial machinery \| Fitness equipment \| Laptop case \| Bushing \| Shell \| Cam \| bearing
Properties:	Chemical resistance \| High rigidity \| wear resistant \| Oil resistant \| high strength \| Thermal stability \| High toughness

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	V-2
UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	V-2
Burning wire flammability index	0.71mm	IEC 60695-2-12	825	°C
	Burning wire flammability index	1.5mm	IEC 60695-2-12	825	°C
	Burning wire flammability index	Burning wire flammability index	3.0mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	0.71mm	IEC 60695-2-13	700	°C
	Hot filament ignition temperature	1.5mm	IEC 60695-2-13	700	°C
	Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC 60695-2-13	700	°C
Extreme Oxygen Index		ISO 4589-2	24	%
UL flame retardant rating	0.71mm	UL 94	V-2
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	23°C	ISO 527-2	3100	Mpa
tensile strength	Yield,23°C	ISO 527-2	85.0	Mpa
tensile strength	tensile strength	Break,23°C	ISO 527-2	55.0	Mpa
Tensile strain	Yield,23°C	ISO 527-2	5.0	%
Nominal tensile fracture strain	23°C	ISO 527-2	25	%
Bending modulus	23°C	ISO 178	2900	Mpa
bending strength	23°C	ISO 178	95.0	Mpa
Poisson's ratio		ISO 527	0.40
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	200	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	70.0	°C
Melting temperature		ISO 11357-3	260	°C
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	1E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	1E-04	cm/cm/°C
RTI Elec	0.71mm	UL 746	140	°C
	RTI Elec	1.5mm	UL 746	140	°C
	RTI Elec	RTI Elec	3.0mm	UL 746	140	°C
RTI Imp	0.71mm	UL 746	95.0	°C
	RTI Imp	1.5mm	UL 746	110	°C
	RTI Imp	RTI Imp	3.0mm	UL 746	110	°C
RTI Str	0.71mm	UL 746	115	°C
	RTI Str	1.5mm	UL 746	125	°C
	RTI Str	RTI Str	3.0mm	UL 746	125	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	23°C,24hr	ISO 62	1.2	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	2.4	%
Shrinkage rate	TD:23°C,2.00mm	ISO 294-4	2.0	%
Shrinkage rate	Shrinkage rate	MD:23°C,2.00mm	ISO 294-4	2.2	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Arc resistance	3.00mm	ASTM D495	PLC6
High arc combustion index	0.71mm	UL 746	PLC 0
	High arc combustion index	1.5mm	UL 746	PLC 0
	High arc combustion index	High arc combustion index	3.0mm	UL 746	PLC 0
High voltage arc tracing rate	HVTR	UL 746	PLC 0
Hot wire ignition	0.71mm	UL 746	PLC 4
	Hot wire ignition	1.5mm	UL 746	PLC 4
	Hot wire ignition	Hot wire ignition	3.0mm	UL 746	PLC 4

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.