Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO 1133 | 12 g/10min |
| Melt volume flow rate | | ISO 1133 | 11.0 cm³/10min |
| Shrinkage rate | | | 0.50to0.70 % |
| Shrinkage rate | | | 0.50to0.70 % |
| Shrinkage rate | | | 0.24 % |
| density | | ISO 1183 | 1.20 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 2300 MPa |
| tensile strength | Yield | ISO 527-2 | 62.0 MPa |
| Tensile strain | Yield | ISO 527-2 | 6.5 % |
| Nominal tensile fracture strain | | ISO 527-2 | 100 % |
| Flexural modulus | | ISO 178 | 2300 MPa |
| bending strength | | ISO 178 | 93.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179 | 65 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179 | NoBreak |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 6E+15 ohms |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 3 |
| Volume resistivity | | IEC 60093 | 3E+16 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 135 °C |
| Heat distortion temperature | | ISO 75-2/A | 122 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 6.5E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 6.6E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.