PBT

PBT 9K22220 4Plas

Properties:
Filler reinforcement material glass beads 20% filler by weight
Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	3.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	4.0 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	3.2mm	UL 94	HB
	UL flame retardant rating	1.6mm	UL 94	HB
		UL flame retardant rating	1.60 mm	UL 94	HB
		UL flame retardant rating	UL flame retardant rating	3.20 mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	23°C	ISO 527-2/5	3250 MPa
tensile strength	Break, 23°C	ISO 527-2/5	55 MPa
Tensile strain	Break, 23°C	ISO 527-2/5	4.0 %
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	3.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	4.0 kJ/m²
Tensile strain	Break,23°C	ISO 527-2/5	4.0 %
Tensile modulus	23°C	ISO 527-2/5	3250 MPa
tensile strength	Break,23°C	ISO 527-2/5	55.0 MPa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	70 °C
	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	170 °C
		Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	170 °C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	70.0 °C
Vicat softening temperature		ISO 306/B	185 °C
Melting temperature		ISO 11357	225 °C
Vicat softening temperature		ISO 306/B	185 °C
Melting temperature		ISO 11357	225 °C

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183	1.45 g/cm³
Shrinkage rate	TD		1.4 %
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.20 %
density		ISO 1183	1.45 g/cm³
Shrinkage rate	TD		1.4 %
Shrinkage rate	Shrinkage rate	MD		1.4 %
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.20 %
water content		ISO 960	<800 ppm

Electrical performance	Test Method	Test Result
Surface resistivity	IEC 60093	1E+14 ohms
Volume resistivity	IEC 60093	1E+16 ohms·cm
Surface resistivity	IEC 60093	1E+14 ohms
Volume resistivity	IEC 60093	1E+16 ohms·cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.