PC IUPILON™ GSH2020DF BK 9001 MITSUBISHI GAS SHANGHAI

Properties:
High temperature resistanwear resistantFiller: Glass fiber reinf20% filler by weight
Usages:
Automotive componentsSpecial for cast film
Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179	46 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.40mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	5700 Mpa
tensile strength	Break	ISO 527-2	74.0 Mpa
Tensile strain	Break	ISO 527-2	2.7 %
Bending modulus		ISO 178	5300 Mpa
bending strength		ISO 178	127 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	133 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	3.4E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	5E-05 cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	140 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	300°C/1.2kg	ISO 1133	11 g/10min
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	10.0 cm3/10min
Shrinkage rate	TD:3.20mm		0.20-0.40 %
	Shrinkage rate	MD:3.20mm		0.20-0.40 %
	Shrinkage rate	Shrinkage rate	吸水率(Saturation,23°C)		0.11 %

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index	CTI	UL 746	PLC 3

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.