| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 294-4 | 0.90 % |
| Shrinkage rate | | ISO 294-4 | 0.40 % |
| Water absorption rate | | ISO 62 | 7.8 % |
| Water absorption rate | | ISO 62 | 2.1 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Burning wire flammability index | | IEC 60695-2-12 | 700 °C |
| flammability | | FMVSS 302 | 0 mm/min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1A/1 | 6900 Mpa |
| Tensile stress | | ISO 527-2/1A/5 | 140 Mpa |
| Tensile strain | | ISO 527-2/1A/5 | 3.0 % |
| Bending modulus 3 | | ISO 178 | 6300 Mpa |
| Bending stress 3 | | ISO 178 | 210 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 40 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 45 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface resistivity 5 | | IEC 60093 | 1.0E+12 ohms |
| Volume resistivity 5 | | IEC 60093 | 1.0E+15 ohms·cm |
| CTI | | IEC 60112 | 500 V |
| injection | Test Condition | Test Method | Test Result |
|---|
| Drying temperature - hot air dryer | | | 80 °C |
| Drying time - hot air dryer | | | 2.0 到 4.0 hr |
| Dew Point - Hot Air Drying Machine | | | -20 °C |
| Suggested maximum moisture content | | | 0.15 % |
| Processing (melt) temperature | | | 280 到 300 °C |
| Temperature | | | 80 到 100 °C |
| injection speed | | | 中等偏快 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO 75-2/Bf | 250 °C |
| | ISO 75-2/Af | 220 °C |
| vicat | | ISO 306/B50 | 240 °C |
| Melting temperature 4 | | ISO 11357-3 | 260 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.