Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| MediumDensity | | | 1.15 g/cm³ |
| melt mass-flow rate | | ISO1133 | 6.0 g/10min |
| Melt volume flow rate | | ISO1133 | 4.30 cm3/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO2039-2 | 69 |
| Rockwell hardness | | ISO2039-2 | 116 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Burning rate 2 | | ISO3795 | <100 mm/min |
| FMVSS flammability | | FMVSS302 | B |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Emission | | VDA275 | <2.00 mg/kg |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179/1eU | 150 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | NoBreak |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 2100 Mpa |
| Tensile stress | | ISO527-2 | 55.0 Mpa |
| Tensile strain | | ISO527-2 | 20 % |
| Nominal tensile fracture strain | | ISO527-2 | 25 % |
| Flexural modulus | | ISO178 | 2000 Mpa |
| Bending stress | | ISO178 | 55.0 Mpa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| AnnealingTemperature | | | 160 °C |
| AnnealingTime-Optional | | | 30.0 min/mm |
| Heat distortion temperature | | ISO75-2/B | 136 °C |
| Heat distortion temperature | | ISO75-2/A | 78.0 °C |
| | ISO11359-2 | 1.1E-04 cm/cm/°C |
| | ISO11359-2 | 1.2E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.