TPU 1190A BASF GERMANY

Form：Granules | Grade：Injection grade

Properties:

High mobilitytransparentLow temperature resistancwear resistant

Typical Applications:

Wire and cableMedical equipment

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Wire and cable \| Medical equipment
Properties:	High mobility \| transparent \| Low temperature resistanc \| wear resistant

Certificates

No Data...

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			用于射出、挤出
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
density		DIN 53479	1.14
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Elongation at Break		DIN 53504-S2	50	%
Elongation at Break	Elongation at Break	80℃水中21天	DIN 53504-S2	600	%
Shore hardness		DIN 53505	92	shoreA
Permanent compression deformation	室温	DIN 53517	25	%
Impact strength of cantilever beam gap	－30℃	DIN 53453	不破裂	KJ/m
Shore hardness		DIN 53505	42	Shore D
Tensile modulus		DIN 53504-S2	16	N/mm
Permanent compression deformation	70℃	DIN 53517	45
tensile strength	80℃水中21天	DIN 53504-S2	35	N/mm
Friction loss		DIN 53516	25	mm
Impact strength of cantilever beam gap	＋23℃	DIN 53453	不破裂	KJ/m
Tensile modulus	20%	DIN 53504-S2	4.5	N/mm
tensile strength		DIN 53504-S2	50	N/mm
tear strength		DIN 53515	65	N/mm
Tensile modulus	100%	DIN 53504-S2	8.5	N/mm
	Tensile modulus	100%	ASTM D412/ISO 527	4.5	Mpa/Psi
	Tensile modulus	Tensile modulus	300%	ASTM D412/ISO 527	8.5	Mpa/Psi
tensile strength		ASTM D412/ISO 527	50	Mpa/Psi
tear strength		ASTM D624/ISO 34	65	n/mm²
Shore hardness		ASTM D2240/ISO 868	92	Shore A
Shore hardness	Shore hardness		ASTM D2240/ISO 868	42	Shore D

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.