PA6 9B23500 X
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO1183 | 1.17 g/cm³ | |
| Shrinkage rate | 1.0 % | ||
| 1.0 % | |||
| Water absorption rate | ISO62 | 2.6 % | |
| density | ISO 1183 | 1.17 g/cm³ | |
| Shrinkage rate | ISO 1183 | 1.0 % | |
| ISO 1183 | 1.0 % | ||
| Water absorption rate | ISO 62 | 2.6 % | |
| Moisture content | ISO960 | <2000 ppm |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 | |
| UL 94 | V-0 | ||
| Burning wire flammability index | IEC 60695-2-12 | 960 °C | |
| Hot filament ignition temperature | IEC 60695-2-13 | 775 °C | |
| UL flame retardant rating | UL 94 | V-0 | |
| UL94 | V-0 | ||
| UL94 | V-0 | ||
| UL94 | V-0 | ||
| Burning wire flammability index | IEC60695-2-12 | 960 °C | |
| Hot filament ignition temperature | IEC60695-2-13 | 775 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/5 | 3500 MPa | |
| Impact strength of cantilever beam gap | ISO 180/1A | 5.0 kJ/m² | |
| ISO 180/1A | 6.0 kJ/m² | ||
| Tensile stress | ISO 527-2/5 | 70.0 MPa | |
| Tensile modulus | ISO527-2/5 | 3500 MPa | |
| Tensile stress | ISO527-2/5 | 70.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO180/1A | 5.0 kJ/m² | |
| ISO180/1A | 6.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 1E+13 ohms | |
| Volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
| CTI | IEC 60112 | 600 V | |
| Surface Resistivity | IEC60093 | 1E+13 ohms | |
| Volume resistivity | IEC60093 | 1E+15 ohms·cm | |
| CTI | IEC60112 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO 75-2/A | 70.0 °C | ||
| melting temperature | ISO 11357 | 223 °C | |
| ISO75-2/A | 70.0 °C | ||
| melting temperature | ISO11357 | 223 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.