PA6 Ultraflow K-FG0-FC NA99001 DSM Additive Manufacturing

Properties:

Filler glass fiber reinforced material 50% filler by weight

Product Description

Certificates(0)

Datasheet

Product Description

Properties:

Filler | glass fiber reinforced material | 50% | filler by weight

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	90	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	85	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	15	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	12	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.6mm	IEC 60695-11-10,-20	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile strain	Break	ISO 527-2	2.5	%
tensile strength	Break	ISO 527-2	220	MPa
Tensile modulus		ISO 527-2	16500	MPa
bending strength		ISO 178	335	MPa
Bending modulus		ISO 178	15500	MPa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	220	°C
Linear coefficient of thermal expansion	TD	ISO 11359-2	5E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	1E-05	cm/cm/°C
Melting temperature		ISO 11357-3	220	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	210	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	MD	ISO 294-4	0.90	%
Shrinkage rate	Shrinkage rate	TD	ISO 294-4	0.90	%
density		ISO 1183	1.56	g/cm³
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	4.5	%
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	1.4	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Relative permittivity	1MHz	IEC 60250	5.20
Relative permittivity	Relative permittivity	100Hz	IEC 60250	3.50
Volume resistivity		IEC 60093	1E+15	ohms·cm
Surface resistivity		IEC 60093	--	ohms
Compared to the anti leakage trace index		IEC 60112	PLC 0
Dissipation factor	1MHz	IEC 60250	0.015
Dissipation factor	Dissipation factor	100Hz	IEC 60250	5E-03

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.