PP Homopolymer Advanced-PP 1102LQ
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 0.910 g/cm³ | |
| melt mass-flow rate | ISO 1133 | 4.5 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 74.0 MPa |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 1500 MPa | |
| tensile strength | Yield | ISO 527-2/50 | 34.0 MPa |
| Tensile strain | Yield | ISO 527-2/50 | 9.0 % |
| Break | ISO 527-2/50 | >50 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 3.5 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179/1eU | 140 kJ/m² | |
| Impact strength of cantilever beam gap | ISO 180/1A | 3.5 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/B | 85.0 °C | |
| vicat | ISO 306/A50 | 154 °C | |
| melting temperature | ISO 3146 | 163 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.