PPO 731S-701 SABIC INNOVATIVE SHANGHAI

Form：Granules | Grade：Injection grade

Properties:

High mobilityAntistaticHigh temperature resistancurrency

Typical Applications:

Food containers

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Food containers
Properties:	High mobility \| Antistatic \| High temperature resistan \| currency

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	5.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	15	kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	5.0	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	15	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2/1	2300	Mpa
tensile strength	Yield	ISO 527-2/50	55.0	Mpa
tensile strength	tensile strength	Break	ISO 527-2/50	50.0	Mpa
Tensile strain	Yield	ISO 527-2/50	5.0	%
Tensile strain	Tensile strain	Break	ISO 527-2/50	30	%
Bending modulus		ISO 178	2200	Mpa
bending strength		ISO 178	75.0	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			100 to 120	°C
drying time			2.0 to 3.0	hr
Hopper temperature			60 to 80	°C
Temperature at the rear of the barrel			240 to 260	°C
Temperature in the middle of the barrel			260 to 280	°C
Temperature at the front of the material cylinder			280 to 300	°C
Spray nozzle temperature			260 to 280	°C
Processing (melt) temperature			280 to 300	°C
Mold temperature			80 to 120	°C
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span	ISO 75-2/Ae	115	°C
Vicat softening temperature	--	ISO 306/B50	135	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	140	°C
Linear coefficient of thermal expansion	Flow : 23 to 80°C	ISO 11359-2	7.0E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 23 to 80°C	ISO 11359-2	7.0E-5	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Melt Volume Flow Rate (MVR)	280°C/5.0 kg	ISO 1133	8.00	cm3/10min
Water absorption rate	Saturation, 23°C	ISO 62	0.23	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.060	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.