Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.30 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 20 g/10min |
| Shrinkage rate | | ASTMD955 | 1.2 % |
| Water absorption rate | | ASTMD570 | <0.20 % |
| Crystallinity | | | <35 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTMD785 | 102 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | Yield | ASTMD790 | 172 MPa |
| Tensile modulus | | ASTMD638 | 3500 MPa |
| tensile strength | Break | ASTMD638 | 97.0 MPa |
| elongation | Break | ASTMD638 | >40 % |
| Flexural modulus | | ASTMD790 | 4000 MPa |
| compressive strength | | ASTMD695 | 124 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 91 J/m |
| Suspended wall beam without notch impact strength | | ASTMD256 | 无断裂 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTMD257 | 2E+16 ohms |
| Volume resistivity | | ASTMD257 | 1E+16 ohms·cm |
| dielectric strength | | ASTMD149 | 18 kV/mm |
| dielectric constant | | ASTMD150 | 3.30 |
| Dissipation Factor | | ASTMD150 | 4E-03 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| thermal conductivity | | ASTMC177 | 0.25 W/m/K |
| melting temperature | | DSC | 340 °C |
| | ASTMD696 | 4.7E-05 cm/cm/°C |
| | ASTMD648 | 160 °C |
| Glass Transition Temperature | | ASTMD3418 | 143 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.