PP FORMULA P ELAN 3003 UV
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 0.900 g/cm³ | |
| melt mass-flow rate | ISO 1133 | 8.0 g/10min | |
| Shrinkage rate | 内部方法 | 1.5to1.8 % | |
| density | ISO 1183 | 0.900 g/cm³ | |
| melt mass-flow rate | ISO 1133 | 8.0 g/10min | |
| Shrinkage rate | 内部方法 | 1.5to1.8 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO 180 | 7.0 kJ/m² | |
| ISO 180 | 35 kJ/m² | ||
| ISO 180 | 7.0 kJ/m² | ||
| ISO 180 | 35 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | ISO 178 | 37.0 MPa | |
| tensile strength | Yield | ISO 527-2 | 18.0 MPa |
| Break | ISO 527-2 | 17.0 MPa | |
| Tensile strain | Break | ISO 527-2 | >400 % |
| Flexural modulus | ISO 178 | 900 MPa | |
| tensile strength | Yield | ISO 527-2 | 18.0 MPa |
| Break | ISO 527-2 | 17.0 MPa | |
| Tensile strain | Break | ISO 527-2 | >400 % |
| Flexural modulus | ISO 178 | 900 MPa | |
| bending strength | ISO 178 | 37.0 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ISO 306/B | 58.0 °C | |
| ISO 306/B | 58.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.