Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.52 g/cm³ |
| Specific volume | | ASTM D792 | 0.650 cm³/g |
| melt mass-flow rate | | ASTM D1238 | 12 g/10min |
| Shrinkage rate | | 内部方法 | 0.30-0.50 % |
| Shrinkage rate | | 内部方法 | 0.50-0.80 % |
| Shrinkage rate | | 内部方法 | 0.50 % |
| Shrinkage rate | | 内部方法 | 0.40-0.60 % |
| Shrinkage rate | | 内部方法 | 0.60-0.90 % |
| Water absorption rate | | ASTM D570 | 0.050 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 125 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 106 Mpa |
| elongation | | ASTM D638 | 3.1 % |
| Flexural modulus | | ASTM D790 | 7810 Mpa |
| bending strength | | ASTM D790 | 174 Mpa |
| Tensile modulus | | ASTM D638 | 8670 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 130 J/m |
| Impact strength of cantilever beam gap | | ASTM D4812 | 860 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| arc resistance | | ASTM D495 | PLC 5 |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 1 |
| High arc combustion index (HAI) | | UL 746 | PLC 2 |
| High Voltage Arc Traceability Rate (HVTR) | | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | | UL 746 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Hot deformation temperature (HDT) | | ASTM D648 | 223 °C |
| Hot deformation temperature (HDT) | | ASTM D648 | 208 °C |
| RTI Elec | | UL 746 | 130 °C |
| RTI Imp | | UL 746 | 130 °C |
| RTI Str | | UL 746 | 140 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.