Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 33 g/10min |
| melt mass-flow rate | | ASTM D1238 | 11 g/10min |
| Melt volume flow rate | | ISO 1133 | 31.0 cm³/10min |
| Melt volume flow rate | | ISO 1133 | 10.0 cm³/10min |
| Shrinkage rate | | ISO 294-4 | 0.70to0.90 % |
| Shrinkage rate | | ISO 294-4 | 0.70to0.90 % |
| Water absorption rate | | ISO 62 | 0.050 % |
| density | | ISO 1183 | 1.21 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180/1A | 55 kJ/m² |
| Impact strength of cantilever beam gap | | ASTM D256 | 140 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 720 J/m |
| Impact strength of cantilever beam gap | | ISO 180/1A | 13 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 2290 MPa |
| Tensile modulus | | ISO 527-2/1 | 2240 MPa |
| tensile strength | | ASTM D638 | 58.0 MPa |
| tensile strength | Yield | ISO 527-2/50 | 57.0 MPa |
| tensile strength | | ASTM D638 | 51.0 MPa |
| tensile strength | Break | ISO 527-2/50 | 49.0 MPa |
| elongation | | ASTM D638 | 9.0 % |
| elongation | Yield | ISO 527-2/50 | 8.9 % |
| elongation | | ASTM D638 | 34 % |
| elongation | Break | ISO 527-2/50 | 33 % |
| Flexural modulus | | ASTM D790 | 2080 MPa |
| Flexural modulus | | ISO 178 | 2210 MPa |
| bending strength | | ISO 178 | 93.0 MPa |
| bending strength | | ISO 178 | 91.0 MPa |
| bending strength | | ASTM D790 | 86.0 MPa |
| bending strength | | ASTM D790 | 84.0 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | 内部方法 | 3.06 |
| Dissipation Factor | | 内部方法 | 9E-04 |
| Dissipation Factor | | 内部方法 | 1.1E-03 |
| Dissipation Factor | | 内部方法 | 1.4E-03 |
| Dissipation Factor | | 内部方法 | 2E-03 |
| dielectric constant | | 内部方法 | 3.04 |
| dielectric constant | | 内部方法 | 3.05 |
| dielectric constant | | 内部方法 | 3.06 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 174 °C |
| Heat distortion temperature | | ISO 75-2/Bf | 175 °C |
| Heat distortion temperature | | ASTM D648 | 154 °C |
| Heat distortion temperature | | ISO 75-2/Af | 155 °C |
| Linear coefficient of thermal expansion | | ASTME831 | 6.5E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ASTME831 | 9.4E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.