Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.18 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 1.7 g/10min |
| melt mass-flow rate | | ISO 1133 | 4.2 g/10min |
| Ethylene content | | 内部方法 | 32.0 mol% |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO 2039-2 | 86 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 2600 MPa |
| tensile strength | Break | ISO 527-2 | 30.0 MPa |
| Tensile strain | Break | ISO 527-2 | 17 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179 | 2.0 kJ/m² |
| film | Test Condition | Test Method | Test Result |
|---|
| OTr | | ISO 14663-2 | 8E-03 cm³·mm/m²/atm/24hr |
| Water Vapor Transmission Rate | | ASTME96 | 1.8 g·mm/m²/atm/24hr |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | ISO 11357-2 | 56.0 °C |
| vicat | | ISO 306 | 162 °C |
| melting temperature | | ISO 11357-3 | 183 °C |
| Crystallization peak temperature | | ISO 11357-3 | 156 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.