Technical Data Sheet
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| colour | | | White |
| colour | | | Yellow |
| density | | | 0.988 g/cm³ |
| density | | | 1.45 g/cm³ |
| density | | | 10到20 Pa·s |
| density | Pot Life | | 2900 min |
| Cured Properties | Test Condition | Test Method | Test Result |
|---|
| Supporting hardness | | | 45 |
| LapShearStrength | | | >13.8 MPa |
| | | 3.42 |
| Volume resistivity | | | >8.0E+12 ohms·cm |
| Dissipation Factor | | | 0.016 |
| physical property | Test Condition | Test Method | Test Result |
|---|
| Particle size | | | <20.0 µm |
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| | | 按重量计算的混合比:100 |
| | | 按重量计算的混合比:6.0 |
| | | 52 wk |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| DegradationTemperature | | | 466 °C |
| Shear Strength | | | 35.2 MPa |
| Operating | | | -55到225 °C |
| Operating | | | -55到325 °C |
| Operating | | | 112 MPa |
| Operating | | | 1.95 |
| WeightLossonHeating | | | 0.080 % |
| WeightLossonHeating | | | 0.17 % |
| WeightLossonHeating | | | 0.35 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | | >15.0 °C |
| | | 6.7E-05 cm/cm/°C |
| | | 1.9E-04 cm/cm/°C |
| Linear coefficient of thermal expansion | | | 0.40 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.