PC Z1-101R SICHUAN ZHONGLAN GUOSU

Form：Granules | Grade：Injection grade

Properties:

Weather resistanceHigh temperature resistanHigh transparencyFatigue resistancehigh strengthHigh impact resistance

Typical Applications:

PlateOffice suppliesElectronic fieldElectrical field

Supplier(1)

Product Description

Certificates(0)

Datasheet

Alternative Model(26)

Product Description

Typical Applications:	Plate \| Office supplies \| Electronic field \| Electrical field
Properties:	Weather resistance \| High temperature resistan \| High transparency \| Fatigue resistance \| high strength \| High impact resistance

Certificates

No Data...

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
purpose			杯子榨汁机壳灯具电器外壳等
Color			透明小蓝底
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Elongation at Break		ASTM D638/ISO 527	84	%
bending strength		ASTM D790/ISO 178	96	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	2442	kg/cm²(MPa)[Lb/in²]
elongation		ASTM D638/ISO 527	60	%
tensile strength		ASTM D638/ISO 527	70	kg/cm²(MPa)[Lb/in²]
Tensile modulus		ASTM D638/ISO 527	2406	kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	70	%
Impact strength of cantilever beam gap		ASTM D256/ISO 179	84P*/505J	kg·cm/cm(J/M)ft·lb/in
Charpy Notched Impact Strength		ASTM D256/ISO 179	87P*	kg·cm/cm(J/M)ft·lb/in
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature		ASTM D1525/ISO R306	150	℃（℉）
Hot deformation temperature	HDT	ASTM D648/ISO 75	124	℃（℉）
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate		ASTM D570/ISO 62	0.1	%
melt mass-flow rate		ASTM D1238/ISO 1133	10.6	g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.