TSU InnoTuf® HP-1090A Innovative Polymers, Inc.

Compare

Technical Data Sheet

Cured Properties	Test Condition	Test Method	Test Result
tear strength		ASTM D624	66.5 kN/m
elongation	Break	ASTM D638	470 %
tensile strength		ASTM D638	31.0 MPa
Shore hardness	ShoreA	ASTM D2240	85to95

Uncured Properties	Test Condition	Test Method	Test Result
viscosity	GelTime		10to16 min
	viscosity	固化时间5		1.8E+02 hr
		viscosity	43°C4		1.5 Pa·s
			viscosity	43°C3		0.85 Pa·s
			viscosity	viscosity	43°C2		0.60 Pa·s

elastomer	Test Condition	Test Method	Test Result
tear strength	Split	ASTM D470	20 kN/m

mechanical properties	Test Condition	Test Method	Test Result
Taber abraser	1000Cycles,1000g,H-18Wheel	ASTM D4060	15.0 mg

thermosetting	Test Condition	Test Method	Test Result
Thermosetting components	Demold Time(66°C)		60to180 min
	Thermosetting components	Hardener		按重量计算的混合比:100按容量计算的混合比:100
	Thermosetting components	Thermosetting components	Resin		按重量计算的混合比:82按容量计算的混合比:77

Physical properties	Test Condition	Test Method	Test Result
density	Cured		1.16 g/cm³
density	density	Hardener		1.13 g/cm³
Shrinkage rate	MD	ASTM D2566	1.0to1.5 %
density	基体Resin		1.20 g/cm³

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.