Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Thermosetting components | | | 按重量计算的混合比:80.按容量计算的混合比:68 |
| Thermosetting components | | | 按重量计算的混合比:100.按容量计算的混合比:100 |
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.04 g/cm³ |
| Shrinkage rate | | 内部方法 | 0.80to0.90 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 94 |
| Shore hardness | | ASTM D2240 | 45 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ASTM D790 | 110 MPa |
| Taber abraser | | ASTM D1044 | 200 mg |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D412 | 16.5 MPa |
| elongation | | ASTM D412 | 250 % |
| tear strength | | ASTM D624 | 78.8 kN/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | ASTM D696 | 1.4E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.