PC/PTFE LNP™ LUBRICOMP™ DL-003 BK1A639
40
- Properties:Thermal stabilityHigh temperature resistan
- Usages:Electronic and Electrical ApplicationsAutomotive componentsEngine parts
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ASTMD955 | 0.80to0.90 % | |
| ISO294-4 | 0.88 % | ||
| ISO294-4 | 0.83 % | ||
| Water absorption rate | ASTMD570 | 0.12 % | |
| ISO62 | 0.15 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam gap impact strength 3 | ISO180/1A | 29 kJ/m² | |
| UnnotchedIzodImpactStrength3 | ISO180/1U | 140 kJ/m² | |
| Dart impact equipped with measuring instruments | ASTMD3763 | 30.6 J | |
| Multi axis Instrumented Impact Energy | ISO6603-2 | 34.1 J |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile strain | ISO527-2 | 5.5 % | |
| elongation | ASTMD638 | 38 % | |
| Flexural modulus | ASTMD790 | 2190 Mpa | |
| ISO178 | 2400 Mpa | ||
| bending strength | ASTMD790 | 80.3 Mpa | |
| Bending stress | ISO178 | 84.1 Mpa | |
| ASTMD3702Modified | 0.18 | ||
| ASTMD3702Modified | 0.070 | ||
| Wear factor - Washer | ASTMD3702Modified | 60.0 10^-10in^5-min/ft-lb-hr | |
| Tensile modulus | ASTMD638 | 2070 Mpa | |
| ISO527-2/1 | 2200 Mpa | ||
| tensile strength | ASTMD638 | 51.7 Mpa | |
| Tensile stress | ISO527-2 | 53.0 Mpa | |
| tensile strength | ASTMD638 | 47.6 Mpa | |
| Tensile stress | ISO527-2 | 50.0 Mpa | |
| elongation | ASTMD638 | 6.1 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ASTMD648 | 128 °C | ||
| Hot deformation temperature 4 | ISO75-2/Af | 131 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.