Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.23 g/cm³ |
| melt mass-flow rate | | ISO1133 | 12 g/10min |
| Shrinkage rate | | 内部方法 | 0.80 % |
| Shrinkage rate | | 内部方法 | 0.70 % |
| Water absorption rate | | ISO62 | 2.0 % |
| Water absorption rate | | ISO62 | 6.5 % |
| Water absorption rate | | ISO62 | <0.10 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-2 |
| UL flame retardant rating | | UL94 | V-2 |
| Burning wire flammability index | | IEC60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 775 °C |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ReinforcementContent | | ISO3451 | 10 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Bending stress | | ISO178 | 110 MPa |
| Tensile modulus | | ISO527-2/1 | 4100 MPa |
| Tensile stress | Break | ISO527-2/50 | 72.0 MPa |
| Tensile strain | Break | ISO527-2/50 | 4.0 % |
| Flexural modulus | | ISO178 | 3800 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 2.5 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 30 kJ/m² |
| Impact strength of cantilever beam gap | | ASTMD256 | 35 J/m |
| Impact strength of cantilever beam gap | | ASTMD256 | 3.50 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| CTI | | IEC60112 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | 160 °C |
| vicat | | ISO306/B50 | 200 °C |
| BallPressure Test | | IEC60695-10-2 | 通过 |
| melting temperature | | ISO11357-3 | 222 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.