Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.31 g/cm³ |
| melt mass-flow rate | | ISO1133 | 19 g/10min |
| Shrinkage rate | | ISO294-4 | 1.6 % |
| Shrinkage rate | | ISO294-4 | 1.7 % |
| Water absorption rate | | ISO62 | 0.40 % |
| Water absorption rate | | ISO62 | 0.20 % |
| viscosity number | | ISO307 | 130 cm³/g |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94,IEC60695-11-10,-20 | HB |
| UL flame retardant rating | | UL94,IEC60695-11-10,-20 | HB |
| Limiting Oxygen Index | | ISO4589-2 | 22 % |
| FMVSS flammability | | FMVSS302 | SE/NBR |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Nominal tensile fracture strain | | ISO527-2 | 30 % |
| Tensile creep modulus | | ISO899-1 | 2600 Mpa |
| Tensile creep modulus | | ISO899-1 | 1800 Mpa |
| Bending stress | | ISO178 | 88.0 Mpa |
| Tensile modulus | | ISO527-2 | 2600 Mpa |
| Tensile stress | | ISO527-2 | 59.0 Mpa |
| Tensile strain | | ISO527-2 | 8.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 3.5 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 4.5 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 无断裂 |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 无断裂 |
| Impact strength of cantilever beam gap | | ISO180/1A | 5.0 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 4.0 kJ/m² |
| | ISO180/1U | 70 kJ/m² |
| | ISO180/1U | 140 kJ/m² |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|
| Melt density | | | 1.11 g/cm³ |
| Ejection Temperature | | | 170 °C |
| SpecificHeatCapacity of Melt | | | 2100 J/kg/°C |
| ThermalConductivityofMelt | | | 0.21 W/m/K |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC60093 | >1.0E+15 ohms·cm |
| dielectric strength | | IEC60243-1 | 26 KV/mm |
| | IEC60250 | 3.80 |
| | IEC60250 | 3.20 |
| Dissipation Factor | | IEC60250 | 2E-03 |
| Dissipation Factor | | IEC60250 | 0.020 |
| CTI | | IEC60112 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 145 °C |
| | ISO75-2/B | 180 °C |
| | ISO75-2/A | 60.0 °C |
| | ISO75-2/A | 60.0 °C |
| vicat | | ISO306/B50 | 175 °C |
| Melting temperature 3 | | ISO11357-3 | 225 °C |
| Crystallization peak temperature 3 | | ISO11357-3 | 192 °C |
| | ISO11359-2 | 1.3E-04 cm/cm/°C |
| | ISO11359-2 | 1.3E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.