PP Homopolymer POLYFORT® FPP 40 GFC HI A SCHULMAN USA

Properties:

Filler glass fiber reinforced material 40% filler by weight

Product Description

Certificates(0)

Datasheet

Product Description

Properties:

Filler | glass fiber reinforced material | 40% | filler by weight

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	57	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	12	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Flammability level	1.5mm	IEC 60695-11-10,-20	HB
Burning rate		ISO 3795	<100	mm/min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Break	ISO 527-2/1A/5	84.0	MPa
Tensile modulus		ISO 527-2/1A/1	7800	MPa
Tensile strain	Break	ISO 527-2/1A/5	4.3	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature	--	ISO 306/B50	131	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/A50	164	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/Af	141	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/Bf	158	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Melt Volume Flow Rate (MVR)	230°C/2.16kg	ISO 1133	3.00	cm³/10min
density		ISO 1183/A	1.23	g/cm³
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		IEC 60093	>1.0E+13	ohms·cm
Surface resistivity		IEC 60093	>1.0E+15	ohms
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test	H358/30	ISO 2039-1	120	MPa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.